<body><script type="text/javascript"> function setAttributeOnload(object, attribute, val) { if(window.addEventListener) { window.addEventListener('load', function(){ object[attribute] = val; }, false); } else { window.attachEvent('onload', function(){ object[attribute] = val; }); } } </script> <div id="navbar-iframe-container"></div> <script type="text/javascript" src="https://apis.google.com/js/platform.js"></script> <script type="text/javascript"> gapi.load("gapi.iframes:gapi.iframes.style.bubble", function() { if (gapi.iframes && gapi.iframes.getContext) { gapi.iframes.getContext().openChild({ url: 'https://www.blogger.com/navbar.g?targetBlogID\x3d8968604820003269863\x26blogName\x3dChemical+%26+Process+Technology\x26publishMode\x3dPUBLISH_MODE_BLOGSPOT\x26navbarType\x3dBLUE\x26layoutType\x3dCLASSIC\x26searchRoot\x3dhttps://webwormcpt.blogspot.com/search\x26blogLocale\x3den\x26v\x3d2\x26homepageUrl\x3dhttp://webwormcpt.blogspot.com/\x26vt\x3d6505904876529004088', where: document.getElementById("navbar-iframe-container"), id: "navbar-iframe" }); } }); </script>

Chemical Process Technology

Continue to learn tips, knowledge and experience about Chemical Process Technology...

Enter your email address:


CLOSE WINDOW


 

Chemical & Process Technology

A place to share knowledge, lesson learnt...

Friday, August 24, 2007


Pitting Corrosion on Metal Surface
Pitting is one of the most destructive forms of corrosion as it will potential cause equipment failures due to perforation / penetration. pitting generally occurs on metal surfaces protected by oxide film such as Stainless steel, aluminum, etc. Typically for boiler and feed water system, pitting corrosion rate increase dramatically with the increase of oxygen content in the fluid.

Pitting can occur in any metal surfaces. Following are some pictures of pitting corrosion.




Pitting corrosion on external pipe surface

Pitting corrosion on external pipe surface



H2S Pitting corrosion on internal pipe surface


Co2 Pitting corrosion on internal pipe surface

Mechanism
Lets look at figure below, oxygen rich fluid in contact with metal surface (at the top of the pit) will becomes the cathode. At the bottom of the pit, low in oxygen level becomes the anode. this will form a complete circuit where metal at the pit (FE) will be ionized to release electron (e) and form ion Ferum (FE2+), this electron will travel to the top of pit to react with Oxygen (O2) (and water, H2O) to form ion hydroxides (OH-). Ion Ferum (FE2+) will react with ion hydroxides (OH-) to form Ferum Oxide (Fe2O3) which typically a brown rust. Deeper the pit leeser the oxygen content and higher the potential and pitting corrosion rate.



Severity of pitting corrosion
Knowing that pitting can cause failure due to perforation while the total corrosion, as measured by weight lossm might be rather minimal, experience shown that rate of penetration may be 10 to 100 times that by general corrosion, pitting corrosion has been considered to be more dangerous than the uniform corrosion damage because it is very difficult to detect, predict and design against. General metal weight loss method almost impossible to detect the internal pitting corrosion.

Pitting corrosion shape
Pits formed due to pitting corrosion can become wide and shallow or narrow and deep which can rapidly perforate the wall thickness of a metal. Following picture demonstrate several types of pitting corrosion shape. This has made it even more difficult to be detected especially undercutting, subsuface and horizontal type.




Preventive measures
There are several preventive approah to avoid pitting. There are :

  • Proper material selection e.g. SS316 with molydenum having higher pitting resistance compare to SS304
  • Use higher alloys (ASTM G48) for increased resistance to pitting corrosion
  • Control oxygen level by injecting oxygen scavenger in boiler water system
  • Control pH, chloride concentration and temperature
  • Cathodic protection and/or Anodic Protection
  • Proper monitoring of oxygen & chloride contents by routine sampling
  • Agitation of stagnant fluid
Related Topics









WebWorm
Continue receive FREE stuff & Update.......Subscribe by Email OR RSS
Any comments / advices ?..........Drop it in comment field (below) or sent a private email to me...

Labels: , , ,

posted by Webworm, 11:04 PM

2 Comments:

Anonymous Anonymous said...

Wow....never thought there are a lot types of pitting corrosion...

Thanks for sharing....

August 26, 2007 at 1:38 AM  
Blogger Webworm said...

Yeap..pitting and crevince corrosion are very nasty and very difficult to tackle...

Do you have any plant experience that you can share with us ?

August 26, 2007 at 2:05 AM  

Post a Comment

Let us know your opinion !!! You can use some HTML tags, such as  <b>, <i>, <a>

Subscribe to Post Comments [Atom]

Home:

<< Home